OK 76.28伊萨焊材

OK 76.28是一款适用于焊接含约2.25Cr-1Mo抗蠕变钢的LMA焊条。该焊条可产生稳定的电弧，飞溅损失较少。OK 76.28可熔敷具有优异抗裂纹性能的焊缝金属。焊缝金属的结垢温度约为625°C。Typical Tensile Properties
PWHT 690°C 1h
Elongation	Tensile Strength	Yield Strength	保护气体
21 %	720 MPa	630 MPa	ISO
-	-	-	AWS

夏比V型缺口冲击性能
PWHT 690°C 1h
Impact Value	Testing Temperature	保护气体
130 J	20 °C	ISO

焊缝金属分析
Mn
Mn	Mo	C	Si	Cr
0.7 %	-	-	-	-
Mo
Mn	Mo	C	Si	Cr
-	1.1 %	-	-	-
C
Mn	Mo	C	Si	Cr
-	-	0.06 %	-	-
Si
Mn	Mo	C	Si	Cr
-	-	-	0.3 %	-
Cr
Mn	Mo	C	Si	Cr
-	-	-	-	2.2 %

熔敷数据
Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
40 sec	0.58 kg	136.0	55-80 A	0.7 kg/h	23 V	2.0 x 300 mm
52 sec	0.58 kg	88.0	70-110 A	0.8 kg/h	25 V	2.5 x 300 mm
62 sec	0.59 kg	49.0	95-150 A	1.2 kg/h	26 V	3.2 x 350 mm
88 sec	0.64 kg	23.0	130-190 A	1.8 kg/h	28 V	4.0 x 450 mm
92 sec	0.64 kg	14.5	150-260 A	2.7 kg/h	29 V	5.0 x 450 mm
90 sec	0.64 kg	10.5	200-350 A	3.9 kg/h	30 V	6.0 x 450 mm