OK 68.15伊萨焊材

OK 68.15是一款用于熔敷铁素体13Cr焊缝金属的不锈钢焊条。OK 68.15适用于当CrNi合金化奥氏体不锈钢焊条无法使用（如结构件将会接触刺激性硫酸气体时）时类似成分钢种的焊接。根据焊接参数不同，结构件及未处理焊缝金属相应的机械性能在相当大的限值范围内变化很大。Typical Tensile Properties
Stress relieved
Stress Relieved Temperature	Stress Relieved Testing Time	保护气体	Elongation	Tensile Strength	Yield Strength
750 °C	6 hr	AWS	-	-	-
750 °C	1 hr	AWS	25 %	520 MPa	370 MPa

夏比V型缺口冲击性能
Stress relieved
Impact Value	Stress Relieved Testing Temp	Stress Relieved Testing Time	Testing Temperature	保护气体
55 J	750 °C	6 hr	20 °C	AWS
35 J	750 °C	6 hr	0 °C	AWS
20 J	750 °C	6 hr	-20 °C	AWS

焊缝金属分析
Mn
Mn	C	Si	Ni	Cr
0.3 %	-	-	-	-
C
Mn	C	Si	Ni	Cr
-	0.04 %	-	-	-
Si
Mn	C	Si	Ni	Cr
-	-	0.4 %	-	-
Ni
Mn	C	Si	Ni	Cr
-	-	-	0.1 %	-
Cr
Mn	C	Si	Ni	Cr
-	-	-	-	12.9 %

熔敷数据
Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
48 sec	0.62 kg	73	65-115 A	1.0 kg/h	25 V	2.5 x 350 mm
71 sec	0.63 kg	33	90-160 A	1.5 kg/h	25 V	3.2 x 450 mm
73 sec	0.57 kg	24	120-220 A	2.0 kg/h	30 V	4.0 x 450 mm