OK 67.60伊萨焊材

可获得**合金化焊缝金属的酸性金红石型药皮焊条。适合将不锈钢焊接到低碳钢和低合金钢上。也适用于在使用不锈钢焊缝金属堆焊低碳钢时的过渡层焊接。Typical Tensile Properties
As welded
Elongation	Tensile Strength	Yield Strength	保护气体
32 %	580 MPa	470 MPa	ISO
-	-	-	AWS

夏比V型缺口冲击性能
As welded
Impact Value	Testing Temperature	保护气体
50 J	20 °C	ISO
40 J	-10 °C	ISO

焊缝金属分析
Mn
Mn	C	Si	Ferrite FN	Ni	N	Cr
0.9 %	-	-	-	-	-	-
C
Mn	C	Si	Ferrite FN	Ni	N	Cr
-	0.03 %	-	-	-	-	-
Si
Mn	C	Si	Ferrite FN	Ni	N	Cr
-	-	0.8 %	-	-	-	-
Ferrite FN
Mn	C	Si	Ferrite FN	Ni	N	Cr
-	-	-	15 %	-	-	-
Ni
Mn	C	Si	Ferrite FN	Ni	N	Cr
-	-	-	-	12.4 %	-	-
Cr
Mn	C	Si	Ferrite FN	Ni	N	Cr
-	-	-	-	-	-	23.7 %

熔敷数据
Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
38 sec	0.60 kg	136	45-65 A	0.7 kg/h	27 V	2.0 x 300 mm
38 sec	0.60 kg	85	45-90 A	1.1 kg/h	28 V	2.5 x 300 mm
51 sec	0.60 kg	45	65-120 A	1.6 kg/h	29 V	3.2 x 350 mm
51 sec	0.60 kg	29	85-180 A	2.5 kg/h	31 V	4.0 x 350 mm
58 sec	0.60 kg	19	110-250 A	3.3 kg/h	32 V	5.0 x 350 mm