OK 67.13伊萨焊材

OK 67.13是一款适用于焊接25Cr20Ni钢的奥氏体不锈钢焊条。焊缝金属抗结垢温度可达1100-1150°C，且不含任何可量度的铁素体。OK 67.13还可用于焊接诸如装甲板等某些风硬钢，以及将不锈钢焊接到非合金钢种上。Typical Tensile Properties
As welded
Elongation	Tensile Strength	Yield Strength	保护气体
35 %	600 MPa	430 MPa	AWS

夏比V型缺口冲击性能
As welded
Impact Value	Testing Temperature	保护气体
90 J	20 °C	AWS

焊缝金属分析
Mn
Mn	C	Si	Ni	Cr
1.9 %	-	-	-	-
C
Mn	C	Si	Ni	Cr
-	0.12 %	-	-	-
Si
Mn	C	Si	Ni	Cr
-	-	0.6 %	-	-
Ni
Mn	C	Si	Ni	Cr
-	-	-	21.1 %	-
Cr
Mn	C	Si	Ni	Cr
-	-	-	-	25.6 %

熔敷数据
Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
42 sec	0.51 kg	101	50-85 A	0.8 kg/h	21 V	2.5 x 300 mm
58 sec	0.51 kg	53	65-120 A	1.2 kg/h	24 V	3.2 x 350 mm
61 sec	0.51 kg	34	70-160 A	1.7 kg/h	28 V	4.0 x 350 mm
67 sec	0.54 kg	21	150-220 A	2.6 kg/h	31 V	5.0 x 350 mm