OK 76.18伊萨焊材

OK 76.18是一款适用于焊接1.Cr-0.5Mo牌号抗蠕变钢的LMA焊条。该焊条可产生稳定的电弧，飞溅损失较少。OK 76.18可熔敷具有抗裂纹和抗气孔特性的焊缝金属。焊缝金属的结垢温度约为575°C。Typical Tensile Properties
PWHT 690°C 1h
Elongation	Tensile Strength	Yield Strength	保护气体
24 %	670 MPa	580 MPa	ISO
-	-	-	AWS

夏比V型缺口冲击性能
PWHT 690°C 1h
Impact Value	Testing Temperature	保护气体
100 J	20 °C	ISO

焊缝金属分析
Mn
Mn	Mo	C	Si	Cr
0.7 %	-	-	-	-
Mo
Mn	Mo	C	Si	Cr
-	0.5 %	-	-	-
C
Mn	Mo	C	Si	Cr
-	-	0.06 %	-	-
Si
Mn	Mo	C	Si	Cr
-	-	-	0.3 %	-
Cr
Mn	Mo	C	Si	Cr
-	-	-	-	1.3 %

熔敷数据
Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
40 sec	0.58 kg	136.0	55-80 A	0.70 kg/h	22 V	2.0 x 300 mm
52 sec	0.58 kg	88.0	70-110 A	0.80 kg/h	24 V	2.5 x 300 mm
65 sec	0.59 kg	49.0	95-150 A	1.10 kg/h	25 V	3.2 x 350 mm
90 sec	0.64 kg	23.0	130-190 A	1.70 kg/h	27 V	4.0 x 450 mm
95 sec	0.64 kg	14.5	150-260 A	2.70 kg/h	28 V	5.0 x 450 mm