OK 48.08伊萨焊材

OK 48.08是适用于诸如海洋工程等苛刻应用的LMA焊条，其具有较佳的机械性能。含有约1% Ni的焊缝金属在温度低至-40°C条件下具有较高的冲击强度。该焊条的药皮为经过抗气孔和氢致裂纹优化的较新一代LMA型号。OK 48.08已经过CTOD测试。Typical Tensile Properties
As welded
Elongation	Tensile Strength	Yield Strength	保护气体
26 %	630 MPa	540 MPa	ISO
-	-	-	AWS

夏比V型缺口冲击性能
As welded
Impact Value	Testing Temperature	保护气体
115 J	-50 °C	ISO
90 J	-60 °C	ISO

焊缝金属分析
Mn
Mn	Mo	C	Si	Ni	Cr
1.2 %	-	-	-	-	-
Mo
Mn	Mo	C	Si	Ni	Cr
-	0.001 %	-	-	-	-
C
Mn	Mo	C	Si	Ni	Cr
-	-	0.06 %	-	-	-
Si
Mn	Mo	C	Si	Ni	Cr
-	-	-	0.35 %	-	-
Ni
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	0.95 %	-
Cr
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	-	0.02 %

熔敷数据
Fusion time per electrode at 90% I max	kg weld metal/kg electrodes	Number of electrodes/kg weld metal	安培	熔敷率	电压 V	直径
42 sec	0.57 kg	135.1	55-80 A	0.60 kg/h	22 V	2.0 x 300 mm
41 sec	0.57 kg	88	75-110 A	1.0 kg/h	27 V	2.5 x 350 mm
66 sec	0.62 kg	42.3	110-150 A	1.30 kg/h	22 V	3.2 x 350 mm
85 sec	0.66 kg	30.0	110-150 A	1.40 kg/h	22 V	3.2 x 450 mm
90 sec	0.69 kg	20.3	150-200 A	2.00 kg/h	22 V	4.0 x 450 mm
85 sec	0.69 kg	14.0	190-275 A	3.00 kg/h	23 V	5.0 x 450 mm